Injection Screw and Barrel/Single Screw and Barrrel for Injection Machine
Stamping parts refer to metal components that are produced through a stamping process. This process involves the use of a stamping press to shape and cut metal sheets into the desired shape and size. Stamping parts are widely used in various industries, including automotive, aerospace, electronics, and construction.Stamping parts are typically made from a range of materials, including aluminum, steel, copper, and brass. The stamping process allows for the production of complex shapes and designs, making it a popular choice for manufacturing parts such as brackets, connectors, and housings.Stamping parts offer several advantages over other manufacturing processes. They are cost-effective, as the stamping process can produce large quantities of parts at a low cost per unit. They are also highly precise, with the ability to produce parts with tight tolerances and high accuracy. Additionally, stamping parts are durable and can withstand harsh environments and extreme temperatures.Overall, stamping parts are an essential component of many industries, providing a reliable and cost-effective solution for producing high-quality metal components. Stamping,Hot Stamping,Metal Stamping,Stamping Press Suzhou Remgar Metal Manufacturer Co.,Ltd. , https://www.remgaral.com
ZY is a very experienced and professional ISO certificated manufacturer for screws and barrels, we have exported our products to 23 different countries with good quality products and serviced.
Pls find the detailed info. For injection screw and barrel as below:
Specification:
Screw diameter: Φ 20mm-Φ 220mm
Mould clamping force: 250T-3200T
Shot weight: 30G-30000G
Technical Information
Base Materials:
1)38CrMoAlA(JIS SACM645)
2)42CrMo(AISI 4140)
Bimetallic alloy materials:
1)Fe-based alloy
2)Ni-based alloy/Deloro alloy
3)Tungsten carbide/Wolfram carbide
Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting
Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000HV
Nitrided brittleness: Less than grade 1
Surface roughness: Ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: >=950HV
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm